2A12 Aluminum is used for the production of various high-load parts and structural parts (but not stamping forgings) such as aircraft fuselage parts, skins, bulkhead, ribs, spars, rivets and other working parts below 150℃.
The 2A12 aluminum sheet is a high-strength alloy extensively used in aerospace, automotive, and industrial sectors. Known for its excellent mechanical properties, good machinability, and
2A12 Aluminum sheet has high strength, good weldability and is heat treatable. It is commonly used in industries such as rivets, wheel hub, missile components and parts, propeller blades, etc.
2A12 or 2A11 aluminium sheet is a 2 series Al-Cu alloy, which mainly contains the alloy component Cu, and belongs to the heat-treated alloy sheet. Advantages of anodized
The 2A12 aluminum sheet is a high-strength duralumin, which can be strengthened by heat treatment and has good spot welding performance. Mingtai Aluminum has focused on the
2A12 or 2A11 aluminium sheet is a 2 series Al-Cu alloy, which mainly contains the alloy component Cu, and belongs to the heat-treated alloy sheet. Therefore, the 2A12 aluminium
2A12: 对应标准: GJB 2053A-2008 航空航天用铝合金结构板规范 Specification for aluminium alloys structural sheet for aerospace: 归类 : 铝及铝合金: 标签: 硬铝 紧固件材料: 说明: 特性：
Aluminum alloy : 2A12 Aluminum sheet : Temper : O, T3, T4, T351, H112 : Thickness (mm) 1.0-600 : Width (mm) 800-2650 : Length (mm) 500-16000 : Application examples : Moulds and
mc Aluminium は、コリンズ エアロスペース、ボーイング、エアバスなどのサプライヤーである、2024 2A12 T3 T4 T351 T851 航空機用アルミニウム シート プレートを生産でき、製品は AMS および EN 規格に適合しています。
As the initial 2A12 aluminum alloy plate was as-rolled in this study, the grains shown in Fig. 3 were squashed and elongated along the rolling direction. The microstructures
2A12 aluminum sheet is a kind of high-strength hard aluminum, which has high plasticity and is easy to be processed into various shapes. This material can be formed through cold working,
2a12铝合金为一种高强度硬铝，可以进行热处理强化；2a12铝合金点焊焊接性良好，用气焊和氩弧焊时有形成晶间裂纹的倾向；2a12铝合金在冷作硬化后可切削性能尚好。抗蚀性不高，常采
2A12 aluminum alloy sheet metal part with a large curvature radius in hot forming-quenching integrated process Wu Pengcheng1,Jin Xiaoyue1, Chen Wei1, Huang Ying1, Li Qiang1, Fan
2A12 aluminium sheet/plate belongs to2 series Al-Cu alloy, which mainly contains the alloy component Cu, and belongs to the heat-treated alloy sheet. Therefore, the 2A12 aluminium